Simüle Edilmiş PWR Birincil Suyu İçinde Uzun Süreli Termal Yaşlandırma Sonrası L-PBF 316L Paslanmaz Çeliklerin Stres Korozyonu Çatlaması Direncinde İşlem Sonrası Bağımlı İyileşme
Post-treatment-dependent improvement in stress corrosion cracking resistance of L-PBF 316L stainless steel after long-term thermal aging in simulated PWR primary water
- 0atıf
- Q1SCImago
- 2026yıl
Kısa özet
Uzun süreli termal yaşlandırma (400 °C, 10.000 saat), lazer toz yatak füzyon (L-PBF) 316L paslanmaz çeliğin stres korozyonu çatlaması (SCC) direncini iyileştirdi; mekanizma işlem sonrası işleme bağlıydı: sıcak izostatik presleme (HIP) Cr tükenmesini azalttı, stres giderme (SR) ise dislokasyon birikimini ve çatlak ilerleme modunu değiştirdi.
Yapay zekâ ile başlık ve abstract'tan üretildi; tam metin okunmaz.
Ana noktalar
- Uzun süreli termal yaşlandırma (400 °C, 10.000 saat) L-PBF 316L paslanmaz çeliğin SCC direncini iyileştirdi.
- Yaşlandırma, HIP işlem görmüş numunelerde tane sınırı Cr tükenmesini azalttı, pasivasyonu teşvik etti ve taneler arası çatlamayı bastırdı.
- Yaşlandırma, SR işlem görmüş numunelerde Cr ayrışmasını ve dislokasyon birikimini azalttı, çatlak ilerlemesini transgranülerden taneler arası kırılmaya kaydırdı.
- Termal yaşlandırmaya verilen SCC tepkisi, işlem sonrası işlemeye bağlı mikroyapısal evrim tarafından yönetilmektedir.
Yapay zekâ ile başlık ve abstract'tan üretildi; tam metin okunmaz.
Özet (abstract)
The effect of long-term thermal aging (400 °C for 10,000 h) on the stress corrosion cracking (SCC) behavior of laser powder-bed fusion 316L stainless steel was investigated in simulated pressurized water reactor (PWR) primary water for two engineering-relevant post-processing conditions: stress relief (SR) and hot isostatic pressing (HIP). Although long-term aging significantly reduced the SCC crack growth rate in both conditions, the mechanisms responsible for this improvement differed fundamentally. In the HIP condition, aging mitigated grain-boundary Cr depletion, promoting local passivation and suppressing preferential intergranular cracking. In the SR condition, aging reduced Cr segregation and geometrically necessary dislocation accumulation at cellular boundaries, thereby relaxing the coupled chemical and mechanical heterogeneities associated with the cellular network and changing the dominant crack propagation mode from transgranular to intergranular cracking. These results demonstrate that the SCC response of L-PBF 316L during service-relevant thermal exposure is governed by post-processing-dependent microstructural evolution rather than a universal aging effect.
Yazarların özeti; kaynağından alınmıştır. Materials Research Letters, 2026 · DOI ↗
Ücretsiz hesapla devam et
Makaleye Sor ile bu makaleye günde 3 soru ücretsiz; makaleyi kaydet, kaynakçasını al, ilgi alanına göre her gün yeni özetler. Çıkarımlar Premium.
Web'de ücretsiz devam etGoogle ya da Apple hesabınla giriş; kart istemez. Bu makaleye geri dönersin.
Telefonda:
Alan: Metaller ve Alaşımlar
Metals and AlloysMaterials Science