Journal of Thermoplastic Composite Materials· 2026Q2
Poliamid 6 Kompozitlerin Hızlandırılmış UV/Yoğuşma ve Dış Hava Koşullarında Eskitme ve Yaşlandırılmış/Geri Dönüştürülmüş Oranlarının Mekanik, Reolojik ve Morfolojik Özelliklere Etkisi: Cam Bilya ve Cam Elyaf Karşılaştırması
Accelerated UV/condensation weathering, outdoor weathering and influence of aged/reprocessed ratios on mechanical, rheological and morphological properties of polyamide 6 composites: Comparing glass bead and glass fiber
- 0atıf
- Q2SCImago
- 2026yıl
Kısa özet
Cam bilya veya elyaf takviyeli geri dönüştürülmüş poliamid 6 (PA6) kompozitler, 12 aylık dış hava koşulları veya 336 saatlik hızlandırılmış UV/yoğuşma eskimesi sonrası azalan mekanik ve reolojik özellikler gösterdi, ancak işlenmemiş polimer ile karıştırılması bu özellikleri kısmen geri kazandırdı.
Yapay zekâ ile başlık ve abstract'tan üretildi; tam metin okunmaz.
Ana noktalar
- Dış hava koşulları ve hızlandırılmış UV/yoğuşma eskimesi, PA6 kompozitlerin mekanik (çekme, darbe, eğilme) ve reolojik özelliklerini azaltmıştır.
- Özellik bozulmasının derecesi, takviye türüne (cam bilya vs. cam elyaf) ve içeriğine (%15 ve %30 ağırlıkça) göre değişiklik göstermiştir.
- Yaşlandırılmış PA6 kompozitlerin %25, %50 ve %75 oranlarında işlenmemiş PA6 ile harmanlanması, mekanik ve reolojik özellikleri kısmen geri kazandırmıştır.
- Eskime ve yeniden işleme sonrası morfolojik değişiklikler de gözlemlenmiştir.
Yapay zekâ ile başlık ve abstract'tan üretildi; tam metin okunmaz.
Özet (abstract)
The usage of polymeric materials is rising, and they are exposed to the effects of light, temperature and water and their combination throughout their lifetime. The increased use of them has caused waste problems. From an environmental point of view, polymer reprocessing (recycling) is one of the good solutions to diminish waste problems. Therefore, in current research, the effect of reprocessing on the mechanical properties (tensile, impact, flexural), melt flow index and morphology was determined for aged polyamide 6 (PA6), glass bead reinforced PA6 composites with 15 and 30 wt% content and glass fiber reinforced PA6 composites with 15 and 30 wt% content. Virgin granules of PA6 and its composites were injection molded to understand the mechanical, rheological, and morphological properties. The samples were then exposed to natural weathering for up to a year in Gebze (Turkey) between August 2018 and August 2019 and artificially accelerated UV/condensation ageing for up to 336 hours in the chamber. After ageing process, naturally and UV aged specimens were ground and the ground specimens were mixed with virgin PA6 or its composites at rates of 25%, 50% and 75% by weight. The mixed polymeric materials were re-molded to manufacture test specimens, and then mechanical, rheological, and morphological properties were determined. Briefly, in current research, the mechanical, rheological, and morphological properties of virgin, aged for 12 months in outdoor environment, aged for 336 hours in UV chamber PA6 or its composites and blends of virgin-aged PA6 or its composites were studied. It was concluded that the change in mechanical and rheological properties varied according to the ageing environment and glass bead or glass fiber content. Generally, mechanical properties diminished with natural and accelerated UV/condensation ageing. But some retention in properties could be obtained with the addition of virgin polymer.
Yazarların özeti; kaynağından alınmıştır. Journal of Thermoplastic Composite Materials, 2026 · DOI ↗
Ücretsiz hesapla devam et
Makaleye Sor ile bu makaleye günde 3 soru ücretsiz; makaleyi kaydet, kaynakçasını al, ilgi alanına göre her gün yeni özetler. Çıkarımlar Premium.
Web'de ücretsiz devam etGoogle ya da Apple hesabınla giriş; kart istemez. Bu makaleye geri dönersin.
Telefonda:
Alan: Polimerler ve Plastikler
Polymers and PlasticsMaterials Science